**奇美ABS PA-757英文物性
| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Specific Gravity
|
1.05
|
g/cm³
|
ASTM D792 |
|
Density
|
1.05
|
g/cm³
|
ISO 1183 |
|
Melt Mass-Flow Rate (MFR) (200°C/5.0 kg)
|
1.8
|
g/10 min
|
ASTM D1238 |
|
Melt Volume-Flow Rate (MVR) (220°C/10.0 kg)
|
22.0
|
cm³/10min
|
ISO 1133 |
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Strength 2 (Yield, 3.18 mm)
|
46.9
|
MPa
|
ASTM D638 |
|
Tensile Stress (Yield)
|
54.0
|
MPa
|
ISO 527-2/50 |
|
Tensile Stress (Break)
|
37.0
|
MPa
|
ISO 527-2/50 |
|
Tensile Elongation 2 (Break, 3.18 mm)
|
20
|
%
|
ASTM D638 |
|
Tensile Strain (Break)
|
20
|
%
|
ISO 527-2/50 |
|
Flexural Modulus 3 (6.35 mm)
|
2620
|
MPa
|
ASTM D790 |
|
Flexural Modulus 4
|
2200
|
MPa
|
ISO 178 |
|
Flexural Strength 5 (6.35 mm)
|
80.4
|
MPa
|
ASTM D790 |
|
Flexural Strength 4
|
76.0
|
MPa
|
ISO 178 |
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Charpy Notched Impact Strength
|
15
|
kJ/m²
|
ISO 179 |
|
Charpy Unnotched Impact Strength
|
No Break
|
ISO 179 | |
|
Notched Izod Impact
|
ASTM D256 | ||
|
23°C, 3.18 mm
|
200
|
J/m
|
|
|
23°C, 6.35 mm
|
180
|
J/m
|
|
|
Notched Izod Impact Strength
|
14
|
kJ/m²
|
ISO 180/1A |
|
Unnotched Izod Impact Strength
|
No Break
|
ISO 180/1U | |
| Hardness |
Nominal Value
|
Unit
|
Test Method
|
|
Rockwell Hardness (R-Scale)
|
116
|
ASTM D785 | |
|
Ball Indentation Hardness (H 358/30)
|
110
|
MPa
|
ISO 2039-1 |
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Deflection Temperature Under Load (1.8 MPa, Unannealed)
|
87.8
|
°C
|
ASTM D648 |
|
Heat Deflection Temperature (1.8 MPa, Unannealed)
|
88.0
|
°C
|
ISO 75-2/A |
|
Deflection Temperature Under Load (1.8 MPa, Annealed)
|
98.9
|
°C
|
ASTM D648 |
|
Heat Deflection Temperature (1.8 MPa, Annealed)
|
98.0
|
°C
|
ISO 75-2/A |
|
Vicat Softening Temperature
|
105
|
°C
|
ASTM D1525 6 |
|
Vicat Softening Temperature
|
|||
|
--
|
104
|
°C
|
ISO 306/A50 |
|
--
|
105
|
°C
|
ISO 306/A120 |
|
--
|
100
|
°C
|
ISO 306/B50 |
|
--
|
101
|
°C
|
ISO 306/B120 |
|
RTI Elec
|
UL 746 | ||
|
1.57 mm
|
85.0
|
°C
|
|
|
3.17 mm
|
85.0
|
°C
|
|
|
RTI Imp
|
UL 746 | ||
|
1.57 mm
|
80.0
|
°C
|
|
|
3.17 mm
|
80.0
|
°C
|
|
|
RTI Str
|
UL 746 | ||
|
1.57 mm
|
85.0
|
°C
|
|
|
3.17 mm
|
85.0
|
°C
|
|
| Electrical |
Nominal Value
|
Unit
|
Test Method
|
|
Arc Resistance
|
PLC 1
|
ASTM D495 | |
|
Comparative Tracking Index (CTI)
|
PLC 0
|
UL 746 | |
|
High Amp Arc Ignition (HAI)
|
UL 746 | ||
|
1.57 mm
|
PLC 0
|
||
|
3.17 mm
|
PLC 0
|
||
|
High Voltage Arc Tracking Rate (HVTR)
|
PLC 1
|
UL 746 | |
|
Hot-wire Ignition (HWI)
|
UL 746 | ||
|
1.57 mm
|
PLC 4
|
||
|
3.17 mm
|
PLC 3
|
||
| Flammability |
Nominal Value
|
Unit
|
Test Method
|
|
Flame Rating
|
UL 94 | ||
|
1.57 mm, ALL
|
HB
|
||
|
1.59 mm
|
HB
|
||
|
3.17 mm, ALL
|
HB
|