| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Specific Gravity
|
0.928
|
g/cm³
|
ASTM D792 |
|
Density
|
0.930
|
g/cm³
|
ISO 1183 |
| Elastomers |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Stress - Across Flow (100% Strain, 23°C)
|
1.90
|
MPa
|
ASTM D412 |
|
Tensile Stress - Across Flow (100% Strain, 23°C)
|
1.90
|
MPa
|
ISO 37 |
|
Tensile Strength - Across Flow (Break, 23°C)
|
3.10
|
MPa
|
ASTM D412 |
|
Tensile Stress - Across Flow (Break, 23°C)
|
3.10
|
MPa
|
ISO 37 |
|
Tensile Elongation - Across Flow (Break, 23°C)
|
360
|
%
|
ASTM D412 |
|
Tensile Elongation - Across Flow (Break, 23°C)
|
360
|
%
|
ISO 37 |
|
Tear Strength - Across Flow 2 (23°C)
|
11.0
|
kN/m
|
ASTM D624 |
|
Tear Strength - Across Flow 3 (23°C)
|
11
|
kN/m
|
ISO 34-1 |
| Hardness |
Nominal Value
|
Unit
|
Test Method
|
|
Shore Hardness (Shore A, 15 sec, 23°C, 2.00 mm)
|
55
|
ISO 868 | |
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
RTI Elec
|
100
|
°C
|
UL 746 |
|
RTI Str
|
85.0
|
°C
|
UL 746 |
| Aging |
Nominal Value
|
Unit
|
Test Method
|
|
Change in Tensile Strength in Air
|
ASTM D573 | ||
|
70°C, 168 hr
|
5.0
|
%
|
|
|
125°C, 168 hr
|
-13
|
%
|
|
|
Change in Tensile Strength in Air
|
ISO 188 | ||
|
70°C, 168 hr
|
5.0
|
%
|
|
|
125°C, 168 hr
|
-13
|
%
|
|
|
Change in Ultimate Elongation in Air
|
ASTM D573 | ||
|
70°C, 168 hr
|
12
|
%
|
|
|
125°C, 168 hr
|
-8.0
|
%
|
|
|
Change in Tensile Strain at Break in Air
|
ISO 188 | ||
|
70°C, 168 hr
|
12
|
%
|
|
|
125°C, 168 hr
|
-8.0
|
%
|
|
|
Change in Durometer Hardness in Air
|
ASTM D573 | ||
|
Shore A, 70°C, 168 hr
|
-1.0
|
||
|
Shore A, 125°C, 168 hr
|
0.0
|
||
|
Change in Shore Hardness in Air
|
ISO 188 | ||
|
Shore A, 70°C, 168 hr
|
-1.0
|
||
|
Shore A, 125°C, 168 hr
|
0.0
|
||
| Electrical |
Nominal Value
|
Unit
|
Test Method
|
|
Comparative Tracking Index (CTI)
|
PLC 0
|
UL 746 | |
|
High Amp Arc Ignition (HAI)
|
PLC 0
|
UL 746 | |
|
High Voltage Arc Resistance to Ignition (HVAR)
|
PLC 5
|
UL 746 | |
|
High Voltage Arc Tracking Rate (HVTR)
|
PLC 1
|
UL 746 | |
|
Hot-wire Ignition (HWI)
|
PLC 3
|
UL 746 | |
| Flammability |
Nominal Value
|
Unit
|
Test Method
|
|
Flame Rating
|
UL 94 | ||
|
1.10 mm
|
HB
|
||
|
1.60 mm
|
HB
|
||
|
3.00 mm
|
HB
|