| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Specific Gravity
|
1.68
|
g/cm³
|
ASTM D792 |
|
Molding Shrinkage - Flow (1.00 mm)
|
0.10
|
%
|
ASTM D955 |
|
Molding Shrinkage - Across Flow (1.00 mm)
|
0.60
|
%
|
ASTM D955 |
|
Water Absorption (Saturation, 41°C)
|
0.90
|
%
|
ASTM D570 |
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Strength
|
175
|
MPa
|
ASTM D638 |
|
Tensile Elongation (Break)
|
2.8
|
%
|
ASTM D638 |
|
Flexural Modulus
|
11000
|
MPa
|
ASTM D790 |
|
Flexural Strength
|
222
|
MPa
|
ASTM D790 |
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Notched Izod Impact
|
100
|
J/m
|
ASTM D256 |
| Hardness |
Nominal Value
|
Unit
|
Test Method
|
|
Rockwell Hardness (R-Scale)
|
125
|
ASTM D785 | |
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Deflection Temperature Under Load (1.8 MPa, Unannealed)
|
285
|
°C
|
ASTM D648 |
|
Glass Transition Temperature (DSC)
|
125
|
°C
|
DSC |
|
Melting Temperature
|
306
|
°C
|
|
| Electrical |
Nominal Value
|
Unit
|
Test Method
|
|
Volume Resistivity
|
1.0E+16
|
ohm·cm
|
ASTM D257 |
|
Dielectric Strength
|
30
|
kV/mm
|
ASTM D149 |
|
Dielectric Constant (1 MHz)
|
3.70
|
ASTM D150 | |
|
Dissipation Factor (1 MHz)
|
0.012
|
ASTM D150 | |
|
Comparative Tracking Index
|
550
|
V
|
IEC 60112 |
| Flammability |
Nominal Value
|
Unit
|
Test Method
|
|
Flame Rating
|
V-0
|
UL 94 |
G2330 日本可乐丽 黑色PA9T 30%玻纤