| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Specific Gravity
|
1.68
|
g/cm³
|
ASTM D792 |
|
Molding Shrinkage - Flow (3.18 mm)
|
0.30
|
%
|
|
|
Molding Shrinkage - Across Flow (3.18 mm)
|
0.50
|
%
|
|
|
Water Absorption (23°C, 24 hr)
|
0.020
|
%
|
ASTM D570 |
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Strength
|
165
|
MPa
|
ASTM D638 |
|
Tensile Stress
|
145
|
MPa
|
ISO 527-2 |
|
Tensile Elongation (Break)
|
1.2
|
%
|
ASTM D638 |
|
Tensile Strain (Break)
|
1.0
|
%
|
ISO 527-2 |
|
Flexural Modulus
|
14500
|
MPa
|
ASTM D790 |
|
Flexural Modulus
|
14000
|
MPa
|
ISO 178 |
|
Flexural Strength
|
221
|
MPa
|
ASTM D790 |
|
Flexural Strength
|
205
|
MPa
|
ISO 178 |
|
Compressive Strength
|
275
|
MPa
|
ASTM D695 |
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Notched Izod Impact (3.18 mm)
|
75
|
J/m
|
ASTM D256 |
|
Notched Izod Impact Strength
|
8.0
|
kJ/m²
|
ISO 180/A |
|
Unnotched Izod Impact (3.18 mm)
|
400
|
J/m
|
ASTM D256 |
|
Unnotched Izod Impact Strength
|
20
|
kJ/m²
|
ISO 180 |
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Deflection Temperature Under Load (1.8 MPa, Annealed)
|
> 260
|
°C
|
ASTM D648 |
|
CLTE - Flow
|
ASTM E831 | ||
|
-50 to 50°C
|
0.000015
|
cm/cm/°C
|
|
|
100 to 200°C
|
0.000015
|
cm/cm/°C
|
|
|
CLTE - Transverse
|
ASTM E831 | ||
|
-50 to 50°C
|
0.000040
|
cm/cm/°C
|
|
|
100 to 200°C
|
0.000080
|
cm/cm/°C
|
|
|
Thermal Conductivity
|
0.31
|
W/m/K
|
|
|
UL Temperature Rating
|
200 to 220
|
°C
|
UL 746B |
| Electrical |
Nominal Value
|
Unit
|
Test Method
|
|
Volume Resistivity
|
1.0E+16
|
ohm·cm
|
ASTM D257 |
|
Dielectric Strength
|
20
|
kV/mm
|
ASTM D149 |
|
Dielectric Constant
|
ASTM D150 | ||
|
26°C, 1 kHz
|
3.90
|
||
|
26°C, 1 MHz
|
3.80
|
||
|
Dissipation Factor
|
ASTM D150 | ||
|
26°C, 1 kHz
|
0.0020
|
||
|
26°C, 1 MHz
|
0.0020
|
||
|
Arc Resistance
|
125
|
sec
|
ASTM D495 |
|
Comparative Tracking Index (CTI)
|
150
|
V
|
UL 746 |
|
Insulation Resistance 2 (90°C)
|
1.0E+12
|
ohm
|
|
| Flammability |
Nominal Value
|
Unit
|
Test Method
|
|
Flame Rating
|
|
UL 94 |
R-4-230BL 美国雪佛龙菲利普PPS 加纤40%