| Physical |
Nominal Value
|
Unit
|
Test Method
|
| Specific Gravity |
1.15
|
g/cm³
|
ASTM D792 |
| Density |
1.16
|
g/cm³
|
ISO 1183 |
| Molding Shrinkage - Flow | Internal Method | ||
|
1.60 mm
|
0.80
|
%
|
|
|
3.20 mm
|
1.1
|
%
|
|
| Molding Shrinkage - Across Flow | Internal Method | ||
|
1.60 mm
|
0.80
|
%
|
|
|
3.20 mm
|
1.1
|
%
|
|
| Molding Shrinkage | ISO 294-4 | ||
|
Across Flow: 2.00 mm
|
1.0
|
%
|
|
|
Flow: 2.00 mm
|
0.90
|
%
|
|
| Water Absorption (23°C, 24 hr) |
1.8
|
%
|
ISO 62 |
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
| Tensile Modulus (23°C) |
3750
|
MPa
|
ISO 527-2 |
| Tensile Strength (23°C) |
89.6
|
MPa
|
ASTM D638 |
| Tensile Stress (Yield, 23°C) |
90.0
|
MPa
|
ISO 527-2/50 |
| Tensile Stress (Break, 23°C) |
80.0
|
MPa
|
ISO 527-2 |
| Tensile Strain (Yield, 23°C) |
4.0
|
%
|
ISO 527-2/50 |
| Tensile Elongation (Break, 23°C) |
14
|
%
|
ASTM D638 |
| Tensile Strain (Break, 23°C) |
10
|
%
|
ISO 527-2 |
| Nominal Tensile Strain at Break (23°C) |
10
|
%
|
ISO 527-2 |
| Flexural Modulus (23°C) |
3450
|
MPa
|
ASTM D790 |
| Flexural Modulus (23°C) |
3660
|
MPa
|
ISO 178 |
| Impact |
Nominal Value
|
Unit
|
Test Method
|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
|
-40°C
|
3.0
|
kJ/m²
|
|
|
23°C
|
3.7
|
kJ/m²
|
|
| Charpy Unnotched Impact Strength (23°C) |
140
|
kJ/m²
|
ISO 179/1eU |
| Notched Izod Impact (23°C) |
43
|
J/m
|
ASTM D256 |
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) |
230
|
°C
|
ASTM D648 |
| Heat Deflection Temperature (0.45 MPa, Unannealed) |
235
|
°C
|
ISO 75-2/B |
| Deflection Temperature Under Load (1.8 MPa, Unannealed) |
70.0
|
°C
|
ASTM D648 |
| Heat Deflection Temperature (1.8 MPa, Unannealed) |
84.0
|
°C
|
ISO 75-2/A |
| Melting Temperature |
264
|
°C
|
ASTM D3418 |
| Melting Temperature 2 |
260
|
°C
|
ISO 11357-3 |
| Flammability |
Nominal Value
|
Unit
|
Test Method
|
| Flame Rating - UL | UL 94 | ||
|
0.750 mm
|
V-0
|
||
|
1.50 mm
|
V-0
|
||
|
3.00 mm
|
V-0
|
||
| Flammability Classification | IEC 60695-11-10, -20 | ||
|
0.750 mm
|
V-0
|
||
|
1.50 mm
|
V-0
|
||
|
3.00 mm
|
V-0
|
||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
|
1.50 mm
|
960
|
°C
|
|
|
3.00 mm
|
960
|
°C
|
|
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
|
1.50 mm
|
775
|
°C
|
|
|
3.00 mm
|
775
|
°C
|
|
| UL |
Nominal Value
|
Unit
|
Test Method
|
| RTI Str | UL 746 | ||
|
0.750 mm
|
85.0
|
°C
|
|
|
1.50 mm
|
85.0
|
°C
|
|
|
3.00 mm
|
85.0
|
°C
|
|
| RTI Imp | UL 746 | ||
|
0.750 mm
|
75.0
|
°C
|
|
|
1.50 mm
|
75.0
|
°C
|
|
|
3.00 mm
|
75.0
|
°C
|
|
| RTI Elec | UL 746 | ||
|
0.750 mm
|
130
|
°C
|
|
|
1.50 mm
|
130
|
°C
|
|
|
3.00 mm
|
130
|
°C
|
|
| Comparative Tracking Index (CTI) (PLC) (3.00 mm) |
PLC 0
|
UL 746 |
FR7025V0F价 PA66 FR7025V0F英文物性