| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Specific Gravity
|
1.16
|
g/cm³
|
ASTM D792 |
|
Density
|
1.17
|
g/cm³
|
ISO 1183 |
|
Melt Mass-Flow Rate (MFR) (260°C/2.16 kg)
|
22
|
g/10 min
|
ASTM D1238 |
|
Melt Volume-Flow Rate (MVR) (260°C/2.16 kg)
|
23.5
|
cm³/10min
|
ISO 1133 |
|
Molding Shrinkage - Flow
|
0.40 to 0.60
|
%
|
ASTM D955 |
|
Water Absorption (23°C, 24 hr)
|
0.40
|
%
|
ASTM D570 |
|
Spiral Flow Length 2 (260°C)
|
157
|
mm
|
Internal Method |
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Strength (Yield, 23°C)
|
49.0
|
MPa
|
ASTM D638 |
|
Tensile Stress (Yield)
|
57.0
|
MPa
|
ISO 527-2/50 |
|
Tensile Stress (Break)
|
45.0
|
MPa
|
ISO 527-2/50 |
|
Tensile Elongation (Break, 23°C)
|
110
|
%
|
ASTM D638 |
|
Tensile Strain (Break)
|
55
|
%
|
ISO 527-2/50 |
|
Flexural Modulus (23°C)
|
2450
|
MPa
|
ASTM D790 |
|
Flexural Modulus 3
|
2600
|
MPa
|
ISO 178 |
|
Flexural Strength (23°C)
|
78.5
|
MPa
|
ASTM D790 |
|
Flexural Strength 3
|
91.0
|
MPa
|
ISO 178 |
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Notched Izod Impact (3.18 mm)
|
710
|
J/m
|
ASTM D256 |
|
Notched Izod Impact Strength
|
50
|
kJ/m²
|
ISO 180/1A |
| Hardness |
Nominal Value
|
Unit
|
Test Method
|
|
Rockwell Hardness (R-Scale)
|
113
|
ASTM D785 | |
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Deflection Temperature Under Load (1.8 MPa, Unannealed)
|
78.0
|
°C
|
ASTM D648 |
|
Heat Deflection Temperature (1.8 MPa, Unannealed)
|
76.0
|
°C
|
ISO 75-2/A |
|
Heat Deflection Temperature (1.8 MPa, Annealed)
|
87.0
|
°C
|
ISO 75-2/A |
|
Vicat Softening Temperature
|
94.0
|
°C
|
ASTM D1525 4 |
|
Vicat Softening Temperature
|
|||
|
--
|
95.0
|
°C
|
ISO 306/A50 |
|
--
|
88.0
|
°C
|
ISO 306/B50 |
|
CLTE - Flow (40 to 100°C)
|
0.000060 to 0.000080
|
cm/cm/°C
|
ASTM D696 |
|
RTI Elec
|
UL 746 | ||
|
1.50 mm
|
60.0
|
°C
|
|
|
2.10 mm
|
60.0
|
°C
|
|
|
2.60 mm
|
60.0
|
°C
|
|
|
3.00 mm
|
60.0
|
°C
|
|
|
RTI Imp
|
UL 746 | ||
|
1.50 mm
|
60.0
|
°C
|
|
|
2.10 mm
|
60.0
|
°C
|
|
|
2.60 mm
|
60.0
|
°C
|
|
|
3.00 mm
|
60.0
|
°C
|
|
|
RTI Str
|
UL 746 | ||
|
1.50 mm
|
60.0
|
°C
|
|
|
2.10 mm
|
60.0
|
°C
|
|
|
2.60 mm
|
60.0
|
°C
|
|
|
3.00 mm
|
60.0
|
°C
|
|
| Electrical |
Nominal Value
|
Unit
|
Test Method
|
|
Arc Resistance
|
PLC 6
|
ASTM D495 | |
|
Comparative Tracking Index (CTI)
|
PLC 0
|
UL 746 | |
|
High Amp Arc Ignition (HAI)
|
UL 746 | ||
|
1.50 mm
|
PLC 0
|
||
|
2.10 mm
|
PLC 0
|
||
|
2.60 mm
|
PLC 0
|
||
|
3.00 mm
|
PLC 0
|
||
|
High Voltage Arc Tracking Rate (HVTR)
|
PLC 2
|
UL 746 | |
|
Hot-wire Ignition (HWI)
|
UL 746 | ||
|
1.50 mm
|
PLC 4
|
||
|
2.10 mm
|
PLC 4
|
||
|
2.60 mm
|
PLC 4
|
||
|
3.00 mm
|
PLC 3
|
||
| Flammability |
Nominal Value
|
Unit
|
Test Method
|
|
Flame Rating
|
UL 94 | ||
|
1.50 mm, ALL
|
V-0
|
||
|
1.59 mm
|
V-0
|
||
|
2.10 mm, ALL
|
|
||
|
2.50 mm, ALL
|
|
||
|
3.00 mm, ALL
|
|
PC/ABS **奇美 PC-510 防火 价格