日本三菱/韩国工程 POM F30-03 英文物性
| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Density
|
1.41
|
g/cm³
|
ISO 1183 |
|
Melt Mass-Flow Rate (MFR)
|
28
|
g/10 min
|
ISO 1133 |
|
Molding Shrinkage - Flow (3.00 mm)
|
2.0
|
%
|
ISO 294-4 |
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Stress (Break, 23°C)
|
65.0
|
MPa
|
ISO 527-2 |
|
Nominal Tensile Strain at Break (23°C)
|
25
|
%
|
ISO 527-2 |
|
Flexural Modulus (23°C)
|
2700
|
MPa
|
ISO 178 |
|
Flexural Strength (23°C)
|
90.0
|
MPa
|
ISO 178 |
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Charpy Notched Impact Strength
|
5.5
|
kJ/m²
|
ISO 179/1eA |
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Heat Deflection Temperature (1.8 MPa, Unannealed)
|
101
|
°C
|
ISO 75-2/A |
| Electrical |
Nominal Value
|
Unit
|
Test Method
|
|
Surface Resistivity
|
1.0E+16
|
ohm
|
IEC 60093 |
|
Volume Resistivity
|
1.0E+14
|
ohm·cm
|
IEC 60093 |
|
Electric Strength
|
19
|
kV/mm
|
IEC 60243-1 |
| Flammability |
Nominal Value
|
Unit
|
Test Method
|
|
Flame Rating
|
HB
|
UL 94 |